A modified corn straw (CS)/epoxy resin (EP) composite was prepared using bisphenol A EP (i.e., E-51) as matrix, 2-methylimidazole as curing agent, and CS modified by 3-glycidyl ether oxypropyl trimethoxysilane (KHCS) as filler. Its chemical structure was characterized by Fourier transform infrared spectroscopy (FTIR). The dynamic thermodynamic properties, mechanical properties, flame retardant property, and fracture morphology were studied using dynamic mechanical analysis (DMA), a universal testing machine, a micro combustion calorimeter, and a scanning electron microscope (SEM), respectively. The effects of different contents of KHCS on various properties were discussed. The experimental result showed that the CS was bonded toKH560 by a covalent bond. The impact strength, tensile strength, and flexural strength of the composites were all improved compared with those of pure EP. When the content of KHCS was 15 wt%, the maximum impact strength of the composites was 3.31 kJ/m2, which was 1.43 times that of the pure EP. The p HRR and THR of MCSEC-20 were 512.44 W/g and 25.03 kJ/g, respectively, which were 40.71% and 27.76% lower than those of pure EP, when the content of KHCS was 20 wt%. Moreover, the mechanism of the curing composites was investigated.
Keywords: composites; corn straw; curing mechanism; epoxy resin; preparation.