Controlling the magnetic ground states at the nanoscale is a long-standing basic research problem and an important issue in magnetic storage technologies. Here, we designed a nanostructured material that exhibits very unusual hysteresis loops due to a transition between vortex and double pole states. Arrays of 700 nm diamond-shaped nanodots consisting of Py(30 nm)/Ru(tRu)/Py(30 nm) (Py, permalloy (Ni80Fe20)) trilayers were fabricated by interference lithography and e-beam evaporation. We show that varying the Ru interlayer spacer thickness (tRu) governs the interaction between the Py layers. We found this interaction mainly mediated by two mechanisms: magnetostatic interaction that favors antiparallel (antiferromagnetic, AFM) alignment of the Py layers and exchange interaction that oscillates between ferromagnetic (FM) and AFM couplings. For a certain range of Ru thicknesses, FM coupling dominates and forms magnetic vortices in the upper and lower Py layers. For Ru thicknesses at which AFM coupling dominates, the magnetic state in remanence is a double pole structure. Our results showed that the interlayer exchange coupling interaction remains finite even at 4 nm Ru thickness. The magnetic states in remanence, observed by magnetic force microscopy (MFM), are in good agreement with corresponding hysteresis loops obtained by the magneto-optic Kerr effect (MOKE) and micromagnetic simulations.
Keywords: interlayer exchange interaction; magnetic nanodots; magnetostatic interaction; nonmagnetic spacers; spin textures.