The van der Waals magnets CrX3 (X = I, Br, and Cl) exhibit highly tunable magnetic properties and are promising candidates for developing novel two-dimensional (2D) spintronic devices such as magnetic tunnel junctions and spin tunneling transistors. Previous studies of the antiferromagnetic CrCl3 have mainly focused on mechanically exfoliated samples. Controlled synthesis of high quality atomically thin flakes is critical for their technological implementation but has not been achieved to date. This work reports the growth of large CrCl3 flakes down to monolayer thickness via the physical vapor transport technique. Both isolated flakes with well-defined facets and long stripe samples with the trilayer portion exceeding 60 µm have been obtained. High-resolution transmission electron microscopy studies show that the CrCl3 flakes are single crystalline in the monoclinic structure, consistent with the Raman results. The room temperature stability of the CrCl3 flakes decreases with decreasing thickness. The tunneling magnetoresistance of graphite/CrCl3 /graphite tunnel junctions confirms that few-layer CrCl3 possesses in-plane magnetic anisotropy and Néel temperature of 17 K. This study paves the path for developing CrCl3 -based scalable 2D spintronic applications.
Keywords: CrCl3; physical vapor transport; tunnel junction; tunneling magnetoresistance; van der Waals magnet.
© 2022 The Authors. Advanced Science published by Wiley-VCH GmbH.