Objectives: Collagen fibrils from carious dentin matrix are prone to enzymatic degradation. This study investigates the feasibility and mechanism of nordihydroguaiaretic acid (NDGA), as a collagen crosslinker, to bio-modify the demineralized dentin matrix.
Methods: The physicochemical properties of the crosslinked dentin matrix were characterized by swelling ratio, ninhydrin assay, Fourier Transform Infrared spectroscopy, and atomic force microscopy. The collagenase degradation resistance was evaluated by measuring loss of dry mass, hydroproline release, loss of elasticity, and micro-nano structure integrity. The cytotoxicity of NDGA-crosslinked dentin collagen was evaluated by flow cytometry.
Results: NDGA crosslinked dentin matrix without destroying the integrity of collagen. Mechanistically, NDGA formed bisquinone bond between two adjacent o-quinone groups, resulting in NDGA polymeric matrix in which collagen fibrils were embedded. NDGA modification could significantly enhance the stiffness of dentin matrix at macro-nano scale. The NDGA-crosslinked dentin matrix exhibited remarkably low collagen degradation and sustained bulk elasticity after collagenase challenge, which were attributed to decreased water content, physical masking of collagenase bind sites on collagen, and improved stiffness of collagen fibrils. Notably, NDGA-crosslinked dentin matrix exhibited excellent biocompatibility.
Conclusion: NDGA, as a biocompatible collagen crosslinker, improves the mechanical properties and biodegradation resistance of demineralized dentin matrix.
Keywords: collagen; crosslink; degradation; nordihydroguaiaretic acid; polyphenols.