The use of radiation is mandatory in modern life, but the harms of radiation cannot be avoided. To minimize the effect of radiation, protection is required for the safety of the environment and human life. Hence, inventing a better shield than a conventional shielding material is the priority of researchers. Due to this reason, this current research deals with an innovative shielding material named EKZ samples having a composition of (epoxy resin (90-40) wt %-kaolin clay (10-25) wt %-ZnO-nano particles (0-35) wt %). The numerous compositional variations of (epoxy resin, kaolin clay, and ZnO-nano particles on the prepared EKZ samples varied the density of the samples from 1.24 to 1.95 g/cm3. The radiation shielding parameter of linear attenuation coefficient (LAC), half value layer (HVL), tenth value layer (TVL), and radiation protection efficiency (RPE) were measured to evaluate the radiation diffusion efficiency of newly made EKZ samples. These radiation shielding parameters were measured with the help of the HPGe detector utilizing the three-point sources (Am-241, Cs-137, and Co-60). The obtained results exposed that the value of linear attenuation coefficient (LAC) and radiation protection efficiency (RPE) was maximum, yet the value of half value layer (HVL), and tenth value layer (TVL), were minimum due to the greater amount of kaolin clay and ZnO-nanoparticles, whereas the amount of epoxy resin was lesser. In addition, it has been clear that as-prepared EKZ samples are suitable for low-dose shielding applications as well as EKZ-35 showed a better shielding ability.
Keywords: ZnO-nanoparticles; epoxy resin; kaolin clay; point sources; radiation shielding.