Low weight and high strength are significant factors in the current decade's spread of composite sandwich materials. Previous studies have proven that forming stiffening ribs in these materials through the Single Point Incremental Forming (SPIF) process is possible and gives encouraging results. On the other hand, knowledge of residual stress (RS) values that form during the manufacturing process is essential, as they may affect the structural integrity of manufactured elements, whether in compression or tension. The investigation of the RS in the composite materials formed by the SPIF process using the XRD method was very limited in the previous studies, so this research aims to apply the X-ray diffraction (XRD) method to determine RS on the part of the LITECOR® sandwich material formed using SPIF. LITECOR® consists of a plastic core between two layers of steel. In this study, three types of LITECOR® were used with differing plastic core thicknesses of 0.8, 1.25, and 1.6 mm, while the steel layers' thickness remained the same at 0.3 mm. The axial and traverse RSs were measured in five positions on both sides of the formed part. It was found that the achieved RSs varied from tensile to compressive along the formed regions. It was found that the residual stress values in both directions were inversely proportional to the thickness of the plastic core. It was noted that the highest RS values were in the unformed base metal, after which the RS was reduced on both sides of the SPIF-formed region, followed by a rise in the RS at the concave of the SPIF-formed region. The maximum measured RS for X-axes was 1041 MPa, whereas, for Y-axes, it was 1260 MPa, both of which were recorded on the back side at a thickness of t = 0.8 mm.
Keywords: LITECOR®; SPIF; X-ray diffraction; XRD; residual stresses; single point incremental.