Styrene-butadiene-styrene block copolymer (SBS) and crumb rubber modifier (CRM) are commonly used modifiers to modify asphalt binders. The aging of modified asphalt binders is an important factor affecting their performance. In this paper, the effects of the two modifiers (i.e., SBS, CRM) on the aging of modified asphalt binders were studied by using low field nuclear magnetic resonance (LF-NMR) technology and dynamic shear rheological (DSR) tests. Test results showed that when T2, a parameter of relaxation time from NMR test, was within 2.2 milliseconds, the relaxation peak of both modified and unmodified asphalt binders tested showed two peaks (i.e., "M" shape), and when it was greater than 2 milliseconds, extra peaks appeared only in the modified asphalts. These extra peaks gradually disappeared with increased aging; the modifiers carried signal intensities of their own. The addition of a modifier changes the law of "the greater the viscosity of asphalt, the shorter the T2 relaxation time". With the aging process, the normalized peak area (NPA) from NMR decreased, and rutting resistance factor from DSR increased. However, the NPA of modified asphalt increased after the PAV test, which may be related to the change of H semaphore. The rheological properties of the asphalt binders before and after aging were well-correlated with the NPA of T2.
Keywords: CRM; SBS; aging; low field nuclear magnetic resonance (LF-NMR); modified asphalt.