A Ni-Cr alloyed layer was prepared on the surface of Q235 steel using double-glow plasma surface alloying (DGPSA) technology and the alloyed layer was cold-rolled with different deformation rates. The microstructure, composition distribution and phase composition of the alloyed layer were characterized using a scanning electron microscope (SEM), an energy dispersive spectrometer (EDS), X-ray diffraction (XRD) and an electrochemical workstation. On this basis, the corrosion resistance of the alloyed layer was analyzed. The results showed that a Ni-Cr alloyed layer formed on the surface of Q235 steel following double-glow plasma nickel-chromium alloying. The alloy elements of Ni and Cr were distributed in a gradient from the outside to the inside and the main phases were FeCr0.29Ni0.16C0.06, Cr23C6 and γ solid solution. The alloyed layer, once cold-rolled with different deformation rates, underwent synchronous plastic deformation with the substrate, with no fracturing and spalling. The self-corrosion potential of the cold-rolled specimens in 5% H2SO4 and 3.5% NaCl solution is close to that of 304L stainless steel, and the corrosion currents are much lower. The corrosion resistance of the cold-rolled specimens is comparable to the original specimens, with no significant changes.
Keywords: Ni-Cr alloying layer; cold rolling; corrosion; double-glow plasma surface alloying.