Dye degradation is a key reaction in organic decomposition production through electron donor transferring. Palladium (Pd) is the best-known element for synthesis Pd-based catalyst, the surface status determines the scope of relative applications. Here we first prepare Pd-Cu alloy nanoparticles (NPs) by co-reduction of Cu(acac)2 (acac = acetylacetonate) and Pd(C5HF6O2)2 in the presence of sodium borohydride (NaBH4) and glutathione (GSH). The obtained Pd-Cu is about ~10 nm with super-hydrophilicity in aqueous mediums. The structural analysis clearly demonstrated the uniform distribution of Pd and Cu element. The colloidal solution keeps stability even during 30 days. Bimetallic Pd-Cu NPs shows biocompatibility in form of cell lines (IMEF, HACAT, and 239 T) exposed to colloidal solution (50 µg mL-1) for 2 days. It shows the catalytic multi-performance for dye degradation such as methyl orange (MO), rhodamine B (RhB), and methylene blue (MB), respectively. The as-synthesized nanoparticles showed one of the best multiple catalytic activities in the industrially important (electro)-catalytic reduction of 4-nitrophenol (4-NP) to corresponding amines with noticeable reduced reaction time and increased rate constant without the use of any large area support. In addition, it exhibits peroxidase-like activity in the 3, 3', 5, 5'-Tetramethylbenzidine (TMB) color test and exhibit obvious difference with previous individual metal materials. By treated with high intensity focused ultrasound filed (HIFU), Pd-Cu NPs might be recrystallized and decreased the diameters than before. The enhancement in catalytic performance is observed obviously. This work expedites rational design and synthesis of the high-hierarchy alloy catalyst for biological and environment-friendly agents.
Keywords: Pd-Cu NPs; biocompatibility; catalytic agent; dye degradation; hydrophilic.