Multipores engineering composed of micro/mesopores is an effective strategy to improve potassium storage performance via providing enormous adsorption sites and shortened ions diffusion distance. However, a detailed exploration of the role played by macropores in potassium storage is still lacking and has been barely reported until now. Herein, a superstructure carbon hexahedron (DGN-900) is synthesized using poly tannic acid (PTA) as precursor. Due to the spatially confined two-step local contraction of PTA along different directions and dimensions during pyrolysis, defective nanosheets with macropores are formed, while realizing a balance between defects content and graphitization degree by regulating temperature. The presence of macropores is conducive to accelerating electrolyte ions rapid infiltration within electrode, and its pore volume can accommodate electrode structure fluctuation upon cycling, while the most suitable ratio of defects to graphitic provides rich ions adsorption sites and sufficient electrons transfer channels, simultaneously. These advantages enable a prominent electrochemical performance in DGN-900 electrode, including high rate (202.9 mAh g-1 at 2 A g-1 ) and long cycling stability over 2000 cycles. This unique fabrication strategy, that is, defects engineering coupled with macropores structure, makes fast and durable potassium storage possible.
Keywords: anode; defect-rich; graphitic structure; macropores; potassium-ion battery.
© 2022 The Authors. Advanced Science published by Wiley-VCH GmbH.