The main feature of perovskite solar cells (PSCs) is that the perovskite layer can be fabricated by the solution method, while the long-time stability of the precursor solution is critical. During the fabrication of formamidinium (FA)-based PSCs, the introduction of methylammonium cations (MA+) in the precursor solution can accelerate the crystallization process of the perovskite layer, stabilize the perovskite structure, and passivate defects. However, MA+ is easy to deprotonate to generate MA molecules, and it then condensates with formamidinium iodide (FAI) to form adverse byproducts. Herein, perovskite microcrystals (MCs) for preparing perovskite precursor solution were investigated in details, which can improve the long-term stability of the precursor solution and the perovskite film. We found that FA+ in MC solution was confined in the three-dimensional scaffold, preventing it from reacting with MA+. Meanwhile, MCs can effectively promote nucleation to form large grains in perovskite films. The photoelectric conversion efficiency (PCE) of the device with 3 week-aged MC solution remains at 90% and is only reduced by 10% after 160 h of continuous operation, which far exceeds the performance of the PCE of those based on mixed monomer powder (MP) solution. Therefore, perovskite MCs, an effective reactive inhibitor to improve the stability of perovskite precursor solutions, are of great significance for large-scale commercial fabrication.
Keywords: inverse temperature crystallization; perovskite microcrystals; perovskite solar cell; solution aging; stability.