Arsenic-alkali residue (AAR) from antimony production can pose significant health and environmental hazards due to the risk of arsenic (As) leaching. In this study, geopolymer composite synthesized from fly ash (FA) was investigated for efficient stabilization of high-arsenic-containing AAR (As2O3 of 22.74 wt%). Two industrial wastes, e.g., granulated blast furnace slag (GBFS) with active calcium composition and water-quenched slag (WQS) from lead-zinc smelting with active iron composition, were investigated for the reinforcement of AAR geopolymer solidification. A wide pH stabilization (from pH = 3-pH = 12) of AAR with the geopolymer composite was successfully achieved, and As leaching concentration of geopolymer with the addition of 5 wt% AAR was significantly reduced from 2343.73 mg/L (AAR) to that below 0.18 mg/L, which successfully meet the regulatory limit of Chinese domestic waste landfill (GB, 18598-2019, 1.2 mg/L) and hazardous waste landfill (GB16889-2008, 0.3 mg/L). Johnbaumite (Ca5(AsO4)3(OH)) was formed in geopolymer composite and leached samples with initial pH from 2.6 to 6 (final pH from 5.54 to 13.15). Magnetite and iron hydroxide phases with strong adsorption and/or As co-precipitation capability were also observed. As stabilization was also achieved with iron oxidation from As(III) to As(V). This study solves the problem of unstable As leaching at different pH for the solidification of arsenic-bearing solid waste, and provides a promising and practical strategy for efficient solidification/stabilization of AAR as well as other similar arsenic-bearing solid wastes with geopolymer composite.
Keywords: Arsenic-alkali residue; Calcium; Geopolymer; Heavy metal; Iron; Solidification/stabilization.
Copyright © 2022. Published by Elsevier Ltd.