Tuning of the electronic and vibrational properties of epitaxial MoS2through He-ion beam modification

Shayani Parida; Yongqiang Wang; Huan Zhao; Han Htoon; Theresa Marie Kucinski; Mikhail Chubarov; Tanushree Choudhury; Joan Marie Redwing; Avinash Dongare; Michael Thompson Pettes

doi:10.1088/1361-6528/aca3af

Tuning of the electronic and vibrational properties of epitaxial MoS₂through He-ion beam modification

Nanotechnology. 2022 Dec 7;34(8). doi: 10.1088/1361-6528/aca3af.

Authors

Affiliations

¹ Center for Integrated Nanotechnologies (CINT), Materials Physics and Applications Division, Los Alamos National Laboratory, NM, United States of America.
² Department of Materials Science and Engineering, University of Connecticut, CT, United States of America.
³ Materials Science in Radiation & Dynamics Extremes (MST-8), Materials Science and Technology Division, Los Alamos National Laboratory, NM, United States of America.
⁴ 2D Crystal Consortium-Materials Innovation Platform, Materials Research Institute, The Pennsylvania State University, University Park, PA 16802, United States of America.
⁵ Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA 16802, United States of America.

PMID: 36395493
DOI: 10.1088/1361-6528/aca3af

Abstract

Atomically thin transition metal dichalcogenides (TMDs), like MoS₂with high carrier mobilities and tunable electron dispersions, are unique active material candidates for next generation opto-electronic devices. Previous studies on ion irradiation show great potential applications when applied to two-dimensional (2D) materials, yet have been limited to micron size exfoliated flakes or smaller. To demonstrate the scalability of this method for industrial applications, we report the application of relatively low power (50 keV)⁴He⁺ion irradiation towards tuning the optoelectronic properties of an epitaxially grown continuous film of MoS₂at the wafer scale, and demonstrate that precise manipulation of atomistic defects can be achieved in TMD films using ion implanters. The effect of⁴He⁺ion fluence on the PL and Raman signatures of the irradiated film provides new insights into the type and concentration of defects formed in the MoS₂lattice, which are quantified through ion beam analysis. PL and Raman spectroscopy indicate that point defects are generated without causing disruption to the underlying lattice structure of the 2D films and hence, this technique can prove to be an effective way to achieve defect-mediated control over the opto-electronic properties of MoS₂and other 2D materials.

Keywords: electronic; epitaxial; ion beam modification; mechanical; optical; two-dimensional; vibrational.