To resolve problems caused by the accumulation of flue gas desulfurization gypsum (FGDG) in the environment, a polymer material was prepared using FGDG, granulated blast furnace slag (GBFS), fly ash (FA), and solid sodium silicate (SSS). The compressive strength of these polymer specimens cured for 3, 28, and 60 d was regularly measured, and their condensation behavior was analyzed. Both the formation behavior of mineral crystals and microstructure characteristics were analyzed further using X-ray diffraction and scanning electron microscopy. The compressive strength of pure FGDG polymer specimen (whose strength is generated by particle condensation crystallization) is insufficient and the condensation is slow. The addition of appropriate amounts of GBFS, FA, and SSS can continuously and considerably improve the compressive strength and shorten the setting time. The optimal proportions of FGDG, GBFS, and FA are 50%, 20%, and 30%, respectively, with the SSS addition amount of 20 g. The incorporation of GBFS, FA, and SSS can promote the polymerization of calcium, silicon, and aluminum in FGDG to form silicate and aluminosilicate minerals. Their formation is the main reason for the increased compressive strength and accelerated coagulation.
Keywords: compressive strength; condensation; flue gas desulfurization gypsum; polymer; slag.