AB-polybenzimidazole (ABPBI) dissolution kinetics in an eco-friendly complex acid-free solvent based on dimethyl sulfoxide (DMSO), methanol and KOH, and the rheological behavior of their solutions are investigated. The optimal component ratio of solvent providing the complete ABPBI dissolution is determined. Methanol containing dissolved KOH contributes to the creation of a single-phase superbasic medium, which accelerates and improves the polymer solubility in a mixture with DMSO, significantly reducing the viscoelasticity of the resulting solution. The optimum methanol content is up to 60 wt.% related to DMSO. The polymer dissolution rate increases by 5 times in this composition. It found the polymer concentration of 9% is close to the dissolution limit due to the strong solution structuring, which is probably associated with an increase in the amount of water released during the KOH-methanol-DMSO interactions. As a result, the conditions for obtaining high concentrated solutions in a complex, mainly organic solvent for fiber spinning are developed. The viscoelastic properties of solutions are measured in the concentration range of 1-9% at temperatures of 20-50 °C. The flow activation energy for 7 and 9% solutions decreases by 1.5 and 2.3 times, respectively, as the content of methanol in the complex solvent increases from 10 to 60%.
Keywords: ABPBI; Poly(2,5(6)-benzimidazole; complex superbasic medium solvents; polymer dopes for spinning; rheology; solubility.