Oxygen evolution reaction is a key process in hydrogen production from water splitting. The development of non-noble metal electrode materials with high efficiency and low cost has become the key factor for large-scale hydrogen production. Binary NiCo-layered double hydroxide (LDH) has been used as a non-noble metal electrocatalyst for OER, but its overpotential is still large. The microstructure of the catalyst is tuned by doping Mo ions into the NiCo-LDH/NF nanowires to form ternary NiCoMo-LDH/NF nanosheet catalysts for the purpose of enhancing the active sites and reducing the initial overpotential. Only 1.5 V (vs. reversible hydrogen electrode (RHE), ≈270 mV overpotential) is required to achieve a catalytic current density of 10 mA cm-2 and a small Tafel slope of 81.46 mV dec-1 in 1 M KOH solution, which manifests the best performance of NiCo-based catalysts reported up to now. Electrochemical analysis and micro-morphology show that the high catalytic activity of NiCoMo-LDH/NF is attributable to the change of the microstructure. The interconnected nanosheet arrays have the obvious advantages of electrolyte diffusion and ion migration. Thus, the active sites of catalysts are significantly increased, which facilitates the adsorption and desorption of intermediates. We conclude that NiCoMo-LDH/NF is a promising electrode material for its low cost and excellent electrocatalytic properties.
Keywords: electrocatalysis; layered double hydroxide; nanosheets; oxygen evolution reaction.