High entropy alloys (HEA) are one of the modern-era alloys accelerating with greater velocity because of their excellent properties and different applications. In the present paper, we have successfully fabricated HEA (23Fe-21Cr-18Ni-20Ti-18Mn) powders by ball milling the elemental Fe, Cr, Ni, Ti, and Mn powders for 15 h. The advancement of the milling process and phase transformation of HEAs were studied by using X-ray diffraction (XRD) and scanning electron microscope (SEM). The crystallite size and the lattice strain of the HEA were calculated by using the Williamson-Hall (W-H) equation and the values were found to be 7 nm and 0.0176%, respectively. Similarly, the true lattice parameter was calculated using the Nelson-Riley (N-R) extrapolation method, and the value was found to be 3.544 Å. We have successfully investigated the electrochemical response of 15 h ball milled 23Fe-21Cr-18Ni-20Ti-18Mn HEA powders to determine the ascorbic acid (AA) using cyclic voltammetry. We have modified the carbon paste electrode with ball milled HEA of concentrations 0, 2, 4, 6, 8, and 10 mg, and among them, 8 mg HEA modified carbon paste electrode (HEA-MCPE) depicted the highest current sensitivity. We reported the effect of modifier concentration, analyte concentration, scan rate, and pH on the oxidation peak of AA. The electrochemical active surface area of carbon paste and MCPE was calculated using the Nernst equation and the values were found to be 0.0014 cm2 and 0.0027 cm2, respectively. The fabricated HEA-MCPE showed excellent current sensitivity, stability, anti-fouling, and selectivity.
Keywords: anodic peak current; ascorbic acid; ball milling; electrochemical sensors; high entropy alloys; microstructure.