Growing thin layers of mixed-metal oxides on titanium supports allows for the preparation of versatile electrodes that can be used in many applications. In this work, electrodes coated with thin films of ruthenium (RuOx) and manganese oxide (MnOx) were fabricated via thermal decomposition of a precursor solution deposited on a titanium substrate by spin coating. In particular, we combined different Ru and Mn precursors, either organic or inorganic, and investigated their influence on the morphology and electrochemical properties of the materials. The tested salts were: Ruthenium(III) acetylacetonate (Ru(acac)3), Ruthenium(III) chloride (RuCl3·xH2O), Manganese(II) nitrate (Mn(NO3)2·4H2O), and Manganese(III) acetylacetonate (Mn(acac)3). After fabrication, the films were subjected to different characterization techniques, including scanning electron microscopy (SEM), polarization analysis, open-circuit potential (OCP) measurements, electrochemical impedance spectroscopy (EIS), linear sweep voltammetry (LSV), cyclic voltammetry (CV), and galvanostatic charge-discharge (GCD) experiments. The results indicate that compared to the others, the combination of RuCl3 and Mn(acac) produces fewer compact films, which are more susceptible to corrosion, but have outstanding capacitive properties. In particular, this sample exhibits a capacitance of 8.3 mF cm-2 and a coulombic efficiency of higher than 90% in the entire range of investigated current densities.
Keywords: manganese oxide; mixed-oxide electrodes; organic and inorganic precursor; ruthenium oxide; spin coating; thin films.