The composite nanomaterials based on noble metals, reducible oxides, and nanostructured carbon are considered to be perspective catalysts for many useful reactions. In the present work, multi-walled carbon nanotubes (MWCNTs) were used for the preparation of Pd-Ce-Ox/MWCNTs and Pt-Ce-Ox/MWCNTs catalysts comprising the active components (6 wt%Pd, 6 wt%Pt, 20 wt%CeO2) as highly dispersed nanoparticles, clusters, and single atoms. The application of X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) provided analysis of the samples’ morphology and structure at the atomic level. For Pd-Ce-Ox/MWCNTs samples, the formation of PdO nanoparticles with an average crystallite size of ~8 nm was shown. Pt-Ce-Ox/MWCNTs catalysts comprised single Pt2+ ions and PtOx clusters less than 1 nm. A comparison of the catalytic properties of the samples showed higher activity of Pd-based catalysts in CO and CH4 oxidation reactions in a low-temperature range (T50 = 100 °C and T50 = 295 °C, respectively). However, oxidative pretreatment of the samples resulted in a remarkable enhancement of CO oxidation activity of Pt-Ce-Ox/MWCNTs catalyst at T < 20 °C (33% of CO conversion at T = 0 °C), while no changes were detected for the Pd-Ce-Ox/MWCNTs sample. The revealed catalytic effect was discussed in terms of the capability of the Pt-Ce-Ox/MWCNTs system to form unique PtOx clusters providing high catalytic activity in low-temperature CO oxidation.
Keywords: MWCNTs; ceria; nanocomposites; palladium; platinum.