As a universal polymer material, polystyrene (PS) is widely applied in electrical devices and construction. Thus, it is necessary to improve the flame retardancy and electromagnetic shielding properties of PS material. In this work, PS/silicon-wrapped ammonium polyphosphate/Inorganic acid-treated multi-walled carbon nanotubes composites (PS/SiAPP/aMWCNT, abbreviated as PAC) were prepared via methods of filtration-induced assembly and hot-pressing. Morphology and structure characterization demonstrated that SiAPP and aMWCNT had good dispersion in PS and excellent compatibility with the PS matrix. Thermogravimetric analysis revealed that the addition of aMWCNT to PS improved its thermal stability and carbon-forming characteristics. The peak heat release rate, the peak carbon monoxide production rate, and the peak smoke production rate of the PAC10 composite decreased by 53.7%, 41.9%, and 45.5%, respectively, while its electromagnetic shielding effectiveness reached 12 dB. These enhancements were attributed to the reason that SiAPP and aMWCNT synergistically catalyzed the char generation and SiAPP produced free radical scavengers and numbers of incombustible gases, which could decrease the oxygen concentration and retard the combustion reaction. Therefore, the assembled PS/SiAPP/aMWCNT system provides a new pathway to improve the flame retardant and electromagnetic shielding properties of PS.
Keywords: electromagnetic interference shielding; flame retardancy; multi-walled carbon nanotube; multiple effects.