Polar poly(vinylidene fluoride) (PVDF) nanotubes have attracted significant attention due to their excellent piezoelectric and ferroelectric properties, yet a tunable fabrication of homogeneous polar PVDF nanotubes remains a challenge. Here, a simple method is reported to fabricate polar PVDF nanotubes using anodize aluminum oxide (AAO) membranes as templates that are removed by etching in a potassium hydroxide (KOH) solution and then ageing at room temperature. PVDF nanotubes originally crystallized in the AAO membrane are pure α-crystals with very low crystallinity, yet after being released from the templates, the crystallinity of the nanotubes markedly increases with ageing at room temperature, leading to the formation of β-PVDF crystals in a very short time, with the formation of γ crystals after longer ageing times. A large amount of γ crystals formed when the released PVDF nanotubes are heated to ≈130 °C. The formation of polar PVDF nanotubes released from the AAO templates treated with higher concentrations of alkaline solution results from the reaction of the surface of the PVDF nanotubes with the alkaline solution and structure reorganization under confined conditions. This large-scale preparation of β- and γ-PVDF opens a new pathway to produce polar PVDF nanomaterials.
Keywords: ageing; alkali treatments; anodized aluminum oxide membranes; polar PVDF nanotubes.
© 2022 Wiley-VCH GmbH.