Coal gasification fine slag (CFS) is a solid contaminant produced by an entrained flow gasifier, which pollutes fields and the air in the long term. CFS is a potential polymer reinforcement filler and has been used in polypropylene and acrylonitrile butadiene styrene resins. Coal gasification fine slag mesoporous silica (FS-SiO2) was prepared by acid leaching, calcination, and pH adjustment, with a larger specific surface area and less surface hydroxyl compared to the commercial precipitated silica (P-silica). The cure characteristics, crosslink density, mechanical properties, the morphology of the tensile fractures, dynamic mechanics, and rubber processing of the prepared styrene butadiene rubber (SBR) composites filled with P-silica and FS-SiO2 were analyzed, respectively. The results indicated that FS-SiO2 was dispersed more uniformly in the SBR matrix than P-silica owing to its smaller amount of surface hydroxyl and spherical structure, resulting in a better mechanical performance and wet skid resistance. In particular, the SBR composites with a filler pH of 6.3 exhibited the highest crosslink density and tensile strength, being superior to commercial P-silica. Significantly, the curing time decreased with the increase in the pH of FS-SiO2, which caused the rubber processing to be more efficient. This strategy can reduce the cost of rubber composites and the environmental pollution caused by CFS.
Keywords: coal gasification fine slag; mechanical properties; promoting vulcanization; styrene butadiene rubber composite; sustainability.