Aluminum dross (AD) is a waste product produced during aluminum processing and can be used to prepare mullite ceramic materials. However, the research on the preparation of mullite porous ceramics entirely from solid waste is still in the development stage. In this paper, porous mullite ceramics were successfully fabricated using a solid-phase sintering process with AD and different silicon sources (fly ash, silica dust, and gangue) as raw materials. The bulk density, apparent porosity, and compressive strength of the specimens were obtained, and the phase compositions and microstructures of the sintered specimens were measured using XRD and SEM, respectively. The average activation energy of the phase transition of fly ash, silica dust, and gangue as silicon sources were 984 kJ/mol, 1113 kJ/mol, and 741 kJ/mol, respectively. The microstructures of the mullite in the specimens were prisms, random aggregates, and needle-shaped, respectively. The formation of needle-shaped mullite combined with the substrate enhanced the mechanical strength of the porous mullite ceramics. The apparent porosity, density, and compressive strength of the specimens with gangue as the silicon source were 33.13%, 1.98 g/cm3, and 147.84 MPa, respectively, when sintered at 1300 °C for 2 h.
Keywords: aluminum dross; mullite; porous ceramics; silicon source.