The corrosion behaviour of (Bi, Pb)-2223 samples compacted at 0.3-1.9 GPa in 0.5 M of HCl, NaCl, and NaOH solutions at 30 °C was investigated using potentiodynamic polarization curves measurements and electrochemical impedance spectroscopy (EIS) technique as well as scanning electron microscopy (SEM) and energy dispersive X-ray emission spectroscopy (EDX). Polarization results showed that the increase in compaction decreases both cathodic hydrogen evolution or oxygen reduction and anodic (BiPb)-2223 superconductor dissolution in 0.5 M HCl, and 0.5 M NaOH. On the other hand, compaction mainly affects the anodic part of the polarization curves of (Bi, Pb)-2223 in 0.5 M NaCl solution. EIS measurements revealed that the highest protection of the superconductors was achieved in 0.5 M NaCl, while the lowest degree of protection was observed in 0.5 M HCl. SEM images show a random plate-like morphology fitted with the marker of (Bi, Pb)-2223 material. The compacted sample at 1.9 GPa indicates deformation of the grains and the formation of a micro-crack. The corrosion mechanism of the superconductor at different pH values was also discussed.
© 2022. The Author(s).