Arsenic removal performance and mechanism from water on iron hydroxide nanopetalines

Abstract

Human health has been seriously endangered by arsenic pollution in drinking water. In this paper, iron hydroxide nanopetalines were synthesized through a precipitation method using KBH₄ and their performance and mechanism of As(V) and As(III) removal were investigated. The prepared material was characterized by SEM-EDX, XRD, BET, zeta potential and FTIR analyses. Batch experiments indicated that the iron hydroxide nanopetalines exhibited more excellent performance for As(V) and As(III) removal than ferrihydrite. The adsorption processes were very fast in the first stage, followed a relatively slower adsorption rate and reached equilibria after 24 h, and the reaction could be fitted best by the pseudo-second order model, followed by the Elovich model. The adsorption isotherm data followed to the Freundlich model, and the maximal adsorption capacities of As(V) and As(III) calculated by the Langmuir model were 217.76 and 91.74 mg/g at pH 4.0, respectively, whereas these values were 187.84 and 147.06 mg/g at pH 8.0, respectively. Thermodynamic studies indicated that the adsorption process was endothermic and spontaneous. The removal efficiencies of As(V) and As(III) were significantly affected by the solution pH and presence of PO₄^3- and citrate. The reusability experiments showed that more than 67% of the removal efficiency of As(V) could be easily recovered after four cycles. The SEM and XRD analyses indicated that the surface morphology and crystal structure before and after arsenic removal were stable. Based on the analyses of FTIR, XRD and XPS, the predominant adsorption mechanism was the formation of inner-sphere surface complexes by the surface hydroxyl exchange reactions of Fe-OH groups with arsenic species. This research provides a new strategy for the development of arsenic immobilization materials and the results confirm that iron hydroxide nanopetalines could be considered as a promising material for removing arsenic from As-contaminated water for their highly efficient performance and stability.