Experimental data on nitrogen adsorption, pellets density and ionic conductivity of nanocomposite solid electrolytes (1−x)LiClO4−xMIL-101(Cr) were interpreted in frames of the model of the composite in which the lithium salt fills the pores of a metal-organic framework MIL-101(Cr). According to the model, the concentration of lithium salt located in the pores reaches a maximum at the concentration x = xmax which is defined by a ratio of the molar volume of LiClO4 and the total volume of accessible pores in the MIL-101(Cr) framework. The model allows one to describe the dependences of pore volume and pellet density on the concentration of MIL-101(Cr). Conductivity of the composites were successfully described by two separate mixing equations for concentration ranges x < xmax and x > xmax. In the first concentration region x < xmax, the composite may be regarded as a mixture of LiClO4 and MIL-101(Cr) with completely filled pores accessible for LiClO4. At x > xmax, the total amount of lithium perchlorate is located in the pores of MIL-101(Cr) and occupies only part of the volume of the accessible pores. It was found that xmax value determined from the concentration dependence of conductivity (xmax = 0.06) is noticeably lower than the corresponding value estimated from adsorption data (xmax = 0.085) indicating a practically complete filling the pores of MIL-101(Cr) in the composite pellets heated before conductivity measurements.
Keywords: MIL-101(Cr); calculation of conductivity; high lithium ion conductivity; metal-organic frameworks; model of composite; nanocomposite solid electrolytes.