Aluminophosphate cement (APC) is a new type of hydraulic cementitious material with many potential functions. Microscopic analysis techniques were used to study the effect of anhydrite on the performance and hydration process of APC under standard curing conditions. The results show that adding an appropriate amount of anhydrite promotes the hydration of APC. The highest compressive strength is reached at an anhydrite content of 15 wt.%. As the anhydrite content increases, the APC's compressive strength decreases. The microscopic analysis of the hydration product morphology shows that the incorporation of anhydrite produces ettringite and other hydration products, improving the microstructure of the cement paste. The mercury intrusion porosimetry results show that the total porosity of the hardened APC paste decreases, and the microstructure becomes denser with an increase in the curing age, resulting in an increase in the compressive strength over time.
Keywords: aluminophosphate cement; anhydrite; compressive strength; hydraulic cementitious material; pore analysis.