The work aimed to produce Ni-P-MoS2-Al2O3 on Al-7075 alloys with multiple attributes through an electroless (EL) plating route. The effects of additives (MoS2 and Al2O3) in the EL bath on the surface morphology, topography, hardness, composition (phase and elemental), roughness, wettability, and coating thickness were evaluated. Results indicate a substantial enhancement in microhardness of the EL-coated surfaces by 70% (maximum hardness = ~316 HV) using powders, and 30% (244 HV) without powders. The maximum coating thickness and water contact angle obtained with powders were 6.16 μm and 100.46°, respectively. The coefficient of friction for the samples prepared using powders was 0.12, and for the base material it was 0.18. The compositional analysis through EDS and XRD suggested the incorporation of a hard and lubricious layer on the EL-coated surface owing to the presence of different phases of Al, Mo, P, Zn, O, and S. Therefore, the resulting coating surfaces impart hardness, self-lubrication, hydrophobicity, and wear resistance simultaneously.
Keywords: coating; composite; electroless plating; lubricant; microhardness; wettability.