(1) Introduction: Implant-supported fixed complete dentures are mostly composed of cantilevers. The purpose of this work was to evaluate the fracture resistance of zirconia (Prettau®, second generation, or Ice Zirkon Translucent, first generation) with cantilever lengths of 6 and 10 mm, and zirconia’s fracture resistance in relation to an average bite force of 250 N. (2) Materials and methods: Forty structures were created in CAD/CAM and divided into four groups: group A (6 mm cantilever in IZT), group B (10 mm cantilever in IZT), group C (6 mm cantilever in Pz), and group D (10 mm cantilever in pz). The study consisted of a traditional “load-to-failure” test. (3) Results: A statistically significant result was found for the effect of cantilever length, t(38) = 16.23 (p < 0.001), with this having a large effect size, d = 4.68. The 6 mm cantilever length (M = 442.30, sd = 47.49) was associated with a higher mean force at break than the 10 mm length (M = 215.18, sd = 40.74). No significant effect was found for the type of zirconia: t(38) = 0.31 (p = 0.757), and d = 0.10. (4) Conclusions: All the components with cantilever lengths of 6 mm broke under forces higher than 250 N. Cantilevers larger than 10 mm should be avoided.
Keywords: CAD/CAM; bite force; cantilever length; fracture; implant-supported prosthesis; zirconia.