Hydrothermal pretreatment (HTP) has long been considered as an efficient and green treatment process on lignocellulosic biomass for bioconversion. However, the variations of cellulose supramolecular structures during HTP as well as their effects on subsequent enzymatic conversion are less understood. In this work, bamboo holocellulose with well-connected cellulose and hemicelluloses polysaccharides were hydrothermally treated under various temperatures. Chemical, morphological, and crystal structural determinations were performed systematically by a series of advanced characterizations. Xylan was degraded to xylooligosaccharides in the hydrolyzates accompanied by the reduced degree of polymerization for cellulose. Cellulose crystallites were found to swell anisotropically, despite the limited decrystallization by HTP. Hydrogen bond linkages between cellulose molecular chains were weakened due to above chemical and crystal variations, which therefore swelled, loosened, and separated the condensed cellulose microfibrils. Samples after HTP present notably increased surface area, favoring the adsorption and subsequent hydrolysis by cellulase enzymes. A satisfying enzymatic conversion yield (>85%) at rather low cellulase enzyme dosage (10 FPU/g glucan) was obtained, which would indicate new understandings on the green and efficient bioconversion process on lignocellulosic biomass.
Keywords: bamboo holocellulose; enzymatic conversion; hydrothermal treatment; supramolecular structures.