Wind power is a promising electricity source. Nevertheless, wind turbine blade icing can cause severe problems in turbine operation. In this study, SiO2 spherical nanoparticles (∼90 nm), produced by RF (radio frequency) plasma spheroidization, were mixed with E51, PDMS, and ethyl acetate, and sprayed on the surface of aluminum plates and regular power windmill fan blades which were already coated with polyurethane primer. XPS and IR spectroscopies revealed the development of SiC and SiPh (Ph = phenolic ring) bonds, whose formation should be favored by the ultrasound and curing processes at 50 °C. The integrity of the coating/substrate interface, whose strength is ascribed to hydrogen bonds, was maintained after 100 icing-melting cycles. The coatings display superhydrophobic behavior and excellent anti-icing performance, along with stability in abrasion, sunlight and self-cleaning ability towards solid pollutants.
Keywords: Anti-icing silica coating; Superhydrophobic; Surface structure; Wind power fan blades.