All-solid-state Li-metal batteries (ASSLBs) are highly desirable, due to their inherent safety and high energy density; however, the irregular and uncontrolled growth of Li filaments is detrimental to interfacial stability and safety. Herein, we report on the incorporation of piezo-/ferroelectric BaTiO3 (BTO) nanofibers into solid electrolytes and determination of electric-field distribution due to BTO inclusion that effectively regulates the nucleation and growth of Li dendrites. Theoretical simulations predict that the piezoelectric effect of BTO embedded in solid electrolyte reduces the driving force of dendrite growth at high curvatures, while its ferroelectricity reduces the overpotential, which helps to regularize Li deposition and Li+ flux. Polarization reversal of soft solid electrolytes was identified, confirming a regular deposition and morphology alteration of Li. As expected, the ASSLBs operating with LiFePO4/Li and poly(ethylene oxide) (PEO)/garnet solid electrolyte containing 10% BTO additive showed a steady and long cycle life with a reversible capacity of 103.2 mAh g-1 over 500 cycles at 1 C. Furthermore, the comparable cyclability and flexibility of the scalable pouch cells prepared and the successful validation in the sulfide electrolytes, demonstrating its universal and promising application for the integration of Li metal anodes in solid-state batteries.
Keywords: lithium dendrite; piezo-ferroelectric effect; solid electrolyte; solid-state battery.