Random isotactic propene-butene copolymers (iPPC4) of different stereoregularity have been synthesized with three different homogeneous single center metallocene catalysts having different stereoselectivity. All samples crystallize from the polymerization solution in mixtures of α and γ forms, and the relative amount of γ form increases with increasing concentrations of butene and of rr stereodefects. All samples crystallize from the melt in mixtures of α and γ forms and the fraction of γ form increases with decreasing cooling rate. At high cooling rates, the crystallization of the α form is always favored, even for samples that contain high total concentration of defects that should crystallize in the γ form. The results demonstrate that in iPPs containing significant concentrations of defects, such as stereodefects and comonomeric units, the γ form is the thermodynamically stable form of iPP and crystallizes in selective conditions of very slow crystallization, whereas the α form is the kinetically favored form and crystallizes in conditions of fast crystallization.
Keywords: melt-crystallization; metallocene catalysts; propylene-butene copolymers; α and γ forms.