Magnetite nanoparticles (MNPs) with 12, 34 and 53 nm sizes have been measured by AC-magnetometry at 50 kHz and 57 mT maximum applied field. The MNPs form chains under the AC-field, and the dynamics of the formation can be studied by measuring hysteresis cycles at different times. The measurement time has been varied from 5 ms to 10 s and for different initial temperatures of 5, 25 and 50 °C. The chain formation, identified by the increase of susceptibility and remanence with the measurement time, appears only for 34 nm particles. It has been observed that saturation, remanence and susceptibility at low (high) fields increase (decrease) with time. For the other two samples, these magnitudes are independent of time. At low fields, the heating efficiency is higher at 5 °C than at 50 °C, whereas it shows an opposite behaviour at higher fields; the origin of this behaviour is discussed in the article. Additionally, the relaxation times, τ N and τ B, have been calculated by considering the influence of the applied field. Chain formation requires translation and rotation of MNPs; therefore, the Brownian mechanism plays a fundamental role. It is found that magnetic reversal for 12 nm MNPs is mainly due to Néel relaxation. However, in the case of 34 nm MNPs, both mechanisms, Néel and Brownian relaxation, can be present depending on the amplitude of the field; for μ 0 H < 22 mT, the physical rotation of the particle is the dominant mechanism; on the other hand, for μ 0 H > 22 mT, both mechanisms are present within the size distribution. This highlights the importance of taking the field intensity into account to calculate relaxation times when analysing the relaxation mechanisms of magnetic colloids subjected to AC fields.
This journal is © The Royal Society of Chemistry.