Ni3Fe/BC nanocatalysts based on biomass charcoal self-reduction achieves excellent hydrogen storage performance of MgH2

Quanhui Hou; Jiaqi Zhang; Zhu'An Zheng; Xinglin Yang; Zhao Ding

doi:10.1039/d2dt02425j

Ni₃Fe/BC nanocatalysts based on biomass charcoal self-reduction achieves excellent hydrogen storage performance of MgH₂

Dalton Trans. 2022 Oct 11;51(39):14960-14969. doi: 10.1039/d2dt02425j.

Authors

Quanhui Hou^{1

2}, Jiaqi Zhang², Zhu'An Zheng¹, Xinglin Yang², Zhao Ding³

Affiliations

¹ School of Automotive Engineering, Yancheng Institute of Technology, Yancheng, 224051, China.
² School of Energy and Power, Jiangsu University of Science and Technology, Zhenjiang, 212003, China. yangxl233@163.com.
³ College of Materials Science and Engineering, National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing, 400044, China. zhaoding@cqu.edu.cn.

PMID: 36111985
DOI: 10.1039/d2dt02425j

Abstract

Bimetallic catalysts offer unique advantages for improving the hydrogen storage performance of MgH₂. Herein, Ni₃Fe/BC nanocatalysts were prepared via a simple solid phase reduction method using a low-cost biomass charcoal (BC) material as the carrier. The onset temperature of hydrogen release for the MgH₂ + 10 wt% Ni₃Fe/BC composite was 184.5 °C, which is 155.5 °C lower than that of pure MgH₂. The dehydrogenated composite starts to absorb hydrogen at as low as 30 °C and is able to absorb 5.35 wt% of H₂ within 10 min under 3 MPa hydrogen pressure at 150 °C. In comparison to pure MgH₂, the apparent activation energies of dehydrogenation and rehydrogenation of MgH₂ + 10 wt% Ni₃Fe/BC were reduced by 52.89 kJ mol^-1 and 23.28 kJ mol^-1, respectively. The hydrogen storage capacity of the composite was maintained in 20 de/rehydrogenation cycles, indicating a good cycling stability. X-Ray diffraction (XRD), transmission electron microscopy (TEM), and X-ray energy dispersive spectroscopy (EDS) characterization reveal that the in situ formation of multiphases Mg₂Ni and Fe catalysts during the hydrogen uptake and release reaction and the transformation of Mg₂Ni/Mg₂NiH₄ together contribute to the superior hydrogen adsorption and desorption performance of MgH₂.