In this study, the influence of carbonate lake sediments (Polylactide/Carbonate Lake Sediments-PLA/CLS) on the mechanical and structural properties of polylactide matrix composites was investigated. Two fractions of sediments originating from 3-8 and 8-12 m were analysed for differences in particle size by distribution (Dynamic Light Scattering-DLS), phase composition (X-ray Diffraction-XRD), the presence of surface functional groups (Fourier Transform-Infrared-FT-IR), and thermal stability (Thermogravimetric Analysis-TGA). Microscopic observations of the composite fractures were also performed. The effect of the precipitate fraction on the mechanical properties of the composites before and after conditioning in the weathering chamber was verified through peel strength, flexural strength, and impact strength tests. A melt flow rate study was performed to evaluate the effect of sediment on the processing properties of the PLA/CLS composite. Hydrophobic-hydrophilic properties were also investigated, and fracture analysis was performed by optical and electron microscopy. The addition of carbon lake sediments to PLA allows for the obtention of composites resistant to environmental factors such as elevated temperature or humidity. Moreover, PLA/CLS composites show a higher flow rate and higher surface hydrophobicity in comparison with unmodified PLA.
Keywords: PLA; calcium carbonate; carbonates; composite; lake sediments; natural filler; polylactide.