The molten salt chlorination method is more suitable to produce TiCl4 using titanium-containing materials with high contents of CaO and MgO in China. However, there is a large amount of molten salt chloride slags generated from the molten salt chlorination process, which contains a variety of chlorides and is difficult to treat, often causing serious environmental problems such as direct piling or landfilling. A novel process was proposed to deal with molten salt chloride slags, and calcium chloride could be effectively removed by this process (as in our previous study). However, magnesium chloride is another impurity which can deteriorate the density and viscosity of the molten salt; it is often found in higher contents, and should be also removed from molten salt chloride slags to efficiently recycle NaCl in novel processes. Na2SiO3 is added to the molten salt chloride slags in the molten state to produce the Mg-containing solid phase, which could be separated with the molten NaCl in novel processes. Thus, the transition of Mg-containing phases and the recovery of NaCl in molten salt chloride slags at high temperature in a novel process were systematically investigated in this work, including thermodynamic analysis, the phase transition behavior of Mg-containing phases, NaCl recovery, etc. The removal rate of Mg was 99.56% when the molar ratio of MgCl2:Na2SiO3 was 1:1.5 at 1273 K and in a N2 atmosphere. The recovery rate of NaCl from the molten salt chlorination slag was 97.62% and the purity of NaCl obtained was 99.35 wt%, which could be used in the molten salt chlorination process.
Keywords: molten salt chloride slags; phases transition of Mg-containing phases; recovery rate of NaCl; removal rate of Mg.