Triple ionic and electronic conductivity (TIEC) in cathode materials for protonic ceramic fuel cells (PCFCs) is a desirable feature that enhances the spatial expansion of active reaction sites for electrochemical oxygen reduction reaction. The realization of optimal TIEC in single-phase materials, however, is challenging. A facile route that facilitates the optimization of TIEC in PCFC cathodes is the strategic development of multiphase cathode materials. In this study, a cubic-rhombohedral TIEC nanocomposite material with the composition Ba(CeCo)0.4 (FeZr)0.1 O3- δ (BCCFZ) is designed via self-assembly engineering. The material consists of a mixed ionic and electronic conducting phase, BaCo1-( x + y + z ) Cex Fey Zrz O3- δ (M-BCCFZ), and a dominant proton-conducting phase, BaCe1-( x + y + z ) Cox Zry Fez O3- δ (H-BCCZF). The dominant cerium-rich H-BCCFZ phase enhances the material's oxygen vacancy concentration and the proton defects formation and transport with a low enthalpy of protonation of -30 ± 9 kJ mol-1 . The area-specific resistance of the BCCFZ symmetrical cell is 0.089 Ω cm2 at 650 °C in 2.5% H2 O-air. The peak power density of the anode-supported single cell based on BCCFZ cathode reaches 1054 mW cm-2 at 650 °C with good operation stability spanning over 500 h at 550 °C. These promote BCCFZ as a befitting cathode material geared toward PCFC commercialization.
Keywords: cathodes; nanocomposites; proton uptake mechanism; protonic ceramic fuel cells; self-assembled; triple ionic and electronic conductivity (TIEC).
© 2022 Wiley-VCH GmbH.