Conventional bioinert bone grafts often have led to failure in osseointegration due to low bioactivity, thus much effort has been made up to date to find alternatives. Recently, MXene nanoparticles (NPs) have shown prominent results as a rising material by possessing an osteogenic potential to facilitate the bioactivity of bone grafts or scaffolds, which can be attributed to the unique repeating atomic structure of two carbon layers existing between three titanium layers. In this study, we produced MXene NPs-integrated the ternary nanofibrous matrices of poly(L-lactide-co-ε-caprolactone, PLCL) and collagen (Col) decorated with MXene NPs (i.e., PLCL/Col/MXene), as novel scaffolds for bone tissue engineering, via electrospinning to explore the potential benefits for the spontaneous osteogenic differentiation of MC3T3-E1 preosteoblasts. The cultured cells on the physicochemical properties of the nanofibrous PLCL/Col/MXene-based materials revealed favorable interactions with the supportive matrices, highly suitable for the growth and survival of preosteoblasts. Furthermore, the combinatorial ternary material system of the PLCL/Col/MXene nanofibers obviously promoted spontaneous osteodifferentiation with positive cellular responses by providing effective microenvironments for osteogenesis. Therefore, our results suggest that the unprecedented biofunctional advantages of the MXene-integrated PLCL/Col nanofibrous matrices can be expanded to a wide range of strategies for the development of effective scaffolds in bone tissue regeneration.
Keywords: Bone tissue engineering; Electrospinning; MXene nanoparticles; Nanofibrous matrices; Osteogenic differentiation.
© 2022. The Author(s).