Calcium alginate capsules encapsulating rejuvenator are a promising self-healing technology for asphalt pavement, but the effects of different healing agents on the self-healing performance of asphalt concrete has not been considered. In view of this, this paper aimed at exploring the effects of calcium alginate capsules containing different healing agents on the self-healing properties of asphalt concrete. Three types of capsules with sunflower oil, waste cooking oil and commercial rejuvenator were fabricated via the orifice-coagulation bath method and the interior structure, mechanical strength, thermal stability and oil content of the prepared capsules were characterized. The healing levels of asphalt mixtures with different capsules under different loading cycles and stress levels were evaluated. Furthermore, the saturates, aromatics, resins and asphaltenes (SARA) fractions and rheological property of extracted asphalt binder within test beams with different capsules after different loading conditions were assessed. The results indicated that all the three types of capsules meet the mechanical and thermal requirement of mixing and compaction of asphalt mixtures. The healing levels of test beams containing vegetable oil capsules were higher than that of waste cooking oil capsules and industrial rejuvenator capsules. The strength recovery ratio and fracture energy recovery ratio of test beams with vegetable oil capsules reached 82.8% and 96.6%, respectively, after 20,000 cycles of compressive loading at 1.4 MPa. The fracture energy recovery ratio of the waste cooking oil capsules also reached as high as 90%, indicating that waste cooking oil can be used as the healing agent of calcium alginate capsules to improve the self-healing property of asphalt mixture. This work provides a significant guide for the selection of healing agent for self-healing capsules in the future.
Keywords: asphalt mixture; calcium alginate capsules; different healing agents; self-healing.