Lithium-sulfur batteries (LSBs) have attracted extensive attention owing to their high energy density and abundant sulfur resources. However, LSBs are still restricted by the unsatisfactory electrochemical performance resulting from the shuttle effect of lithium polysulfide (LiPSs), and the potential fire hazard caused by inflammable ether electrolytes and polyolefin separators. Herein, a facile immobilization strategy for hexachlorocyclotriphosphazene (HCCP) is creatively applied to address the above issues simultaneously. Insoluble HCCP cross-linked microspheres (H-CMP) are firstly obtained at ambient temperature using tannic acid (TA) as a cross-linking agent and then a multifunctional separator coating is constructed based on H-CMP. The released phosphorus-related radicals from H-CMP in wide temperatures effectively prevent the combustion of electrolytes and separators, and hence improve the fire safety of the Li-S pouch cell. Furthermore, H-CMP availably chemisorbs LiPSs to interdict the shuttle effect, thereby dramatically improving the electrochemical performance of LSBs. The effectiveness of this strategy is also verified in high sulfur loading (6.38 mg cm-2 ), high temperature (50 °C), and Li-S pouch cells. More importantly, H-CMP exhibits sufficient stability for Li metal and suppression of Li dendrites. This facile immobilization strategy for multifunctional phosphazenes provides a competitive option for the large-scale fabrication of high-safety and high-performance LSBs.
Keywords: flame retardancy; lithium anode stabilization; lithium polysulfide; lithium-sulfur batteries; phosphazene.
© 2022 Wiley-VCH GmbH.