Evaluation of Micro- and Nano-Bismuth(III) Oxide Coated Fabric for Environmentally Friendly X-Ray Shielding Materials

ACS Omega. 2022 Aug 1;7(32):28248-28257. doi: 10.1021/acsomega.2c02578. eCollection 2022 Aug 16.

Authors

Supranee Kaewpirom¹, Khaisang Chousangsuntorn², Siridech Boonsang³

Affiliations

¹ Department of Chemistry, Faculty of Science, Burapha University, Chonburi 20131, Thailand.
² Department of Radiological Technology, Faculty of Medical Technology, Mahidol University, Nakhon Pathom 73170, Thailand.
³ Department of Electrical Engineering, School of Engineering, King Mongkut's Institute of Technology Ladkrabang, Bangkok 10520, Thailand.

Abstract

This research focuses on the development of environmentally friendly textile-based shielding composites, from micro-sized and nanosized Bi₂O₃ particles, against ionizing radiation. Polyester fabric dyne-coated with either micro- or nano-Bi₂O₃ particles shields some X-rays but the effectiveness is poor. With only ∼58% uptake of micro-sized Bi₂O₃ particles dyeing on polyester fabric, the insufficient amount of Bi₂O₃ leaded to the low density of particles, resulting in only 30% of X-ray shielding at 80 kVp. Cotton fabric coated with either micro- or nano-Bi₂O₃/poly(vinyl alcohol) (PVA) composites, on the other hand, demonstrated the capacity to attenuate X-ray generated by high diagnostic X-ray tube voltages of 70-100 kVp, in compliance with medical protection requirements. The X-ray attenuation performance of cotton fabric coated with either micro-Bi₂O₃/PVA or nano-Bi₂O₃/PVA nanocomposite decreased progressively with increasing tube acceleration voltages, however their ionizing radiation-shielding performance enhanced with the number of fabric layers. Interestingly, for all X-ray tube voltages evaluated, the micro-Bi₂O₃/PVA composite outperformed the nano- Bi₂O₃/PVA composite in terms of X-ray shielding. At a weight ratio of 66.7% Bi₂O₃, 10 layers of cotton fabric coated with micro- Bi₂O₃/PVA composite can attenuate 90, 85, and 80% of X-ray photons at 70, 80, and 100 kVp, respectively. As a result, these less harmful X-ray shielding materials have the potential to replace lead-based composites, which are highly toxic to human health and have negative environmental consequences.