In this work, physical cross-linking was used to create nanocomposite hydrogels composed of unmodified gum arabic (GA), chitosan (Ch), and natural nanohydroxyapatite (nHA), using an acrylic acid (AA) solvent. Different GA/chitosan contents (15%, 25%, and 35% of the used AA) as well as different nHA contents (2, 5, and 10 wt.%), were used and studied. The natural nHA and the fabricated GA/Ch/nHA nanocomposite hydrogels were characterized using different analysis techniques. Using acrylic acid solvent produced novel hydrogels with compressive strength of 15.43-22.20 MPa which is similar to that of natural cortical bone. The addition of natural nHA to the hydrogels resulted in a significant improvement in the compressive strength of the fabricated hydrogels. In vitro studies of water absorption and degradation-and in vivo studies-confirmed that the nanocomposite hydrogels described here are biodegradable, biocompatible, and facilitate apatite formation while immersed in the simulated body fluid (SBF). In light of these findings, the GA/Ch/nHA nanocomposite hydrogels are recommended for preparing bioactive nanoscaffolds for testing in bone regeneration applications.
Keywords: acrylic acid; bone regeneration; chitosan; composite scaffold; hydrogel; natural nanohydroxyapatite; unmodified gum arabic.