The development of laser powder bed fusion (LPBF) additive manufacturing techniques for microfabrication raises the need for the employment of new process configurations and parameters. In this study, micro-LPBF of Ni-based superalloy Inconel 718 using a spot laser of 30 µm was examined. The response surface method with a central composite design was employed to determine the optimum process parameter. A wide range of heat treatment cycles was applied to additively manufacture Inconel samples. The mechanical behavior of heat-treated Inconel 718 parts fabricated via micro-LPBF was investigated and correlated to the microstructural characteristics. The result showed that using optimum input energy density led to a homogenous distribution of nanosized (<10 nm) circular γ′ and plate-like γ″ particles in the γ matrix. Uniaxial tensile tests on heat-treated samples showed that ageing temperature is the most determinant factor in the mechanical strength of additively manufactured Inconel 718.
Keywords: Ni-based superalloys; heat treatment; mechanical properties; micro laser powder bed fusion.