Cooling based on the electrocaloric effect (ECE) is a promising solution to environmental and energy efficiency problems of vapor-compression refrigeration. Ferroelectric polymer-ceramics nanocomposites, integrating high electric breakdown of organic ferroelectrics and large EC strength of ceramics, are attractive EC materials. Here, we tuned the orientation of Ba0.67Sr0.33TiO3 nanofibers (BST nfs) in the P(VDF-TrFE-CFE) polymer. When the nfs were aligned parallel to the field, a ΔT of 11.3 K with an EC strength of 0.16 K·m/MV was achieved in the blends. The EC strength not only surpasses advanced nanocomposites but also is comparable to ferroelectric ceramics. The simulation indicates that a significantly higher electric field is concentrated in polymer regions around the ends of the orientated nfs, contributing to easier flipping of polymer chains for large ECE. This work provides a new method to obtain large ECE in composites for next-generation refrigeration.
Keywords: electrocaloric effect; nanocomposites; orientation; terpolymer.