Bi-doped yttrium iron garnet nanopowders were successfully synthesized by a combustion method at different synthesis conditions, and the evolution of their structural, magnetic, and magneto-optical properties has been studied by various methods. X-ray diffraction analysis revealed that crystallite size increases with increase as in annealing time (tA) well as in annealing temperature (TA) and varied from 15.2 nm (TA = 650 °C, tA = 0.5 h) to 44.5 nm (TA = 800 °C, tA = 12 h). The magnetic hysteresis loops exhibit behavior characteristic of soft magnetic materials; herewith, the saturation magnetization demonstrates a growing trend with increasing crystallite size (D). The behavior of the coercivity indicates that, at room temperature, the transition between single-domain and multidomain states occurs at D = 35.3 nm. It was found that the size effect in the MCD spectra is clearly observed for the samples with crystallite sizes less than 42.2 nm for an intersublattice charge-transfer transition and a crystal-field tetrahedral transition. The influence of cation redistribution on the observed changes has been discussed.
Keywords: Bi-YIG; Combustion method; MCD spectroscopy; Magnetic properties; Nanopowders.
© 2022. The Author(s).