Treating and utilizing heavy metal enriched plants have become growing problems. In this work, a series of composite foams were made from the powder of Cadmium-rich plant, polyacrylonitrile (PAN) and polyurethane (PU). Test results indicated that the addition of plant powder can not only increase the specific surface area, but also improve the apparent density and thermal stability of the foams. Besides, compared with the foam without plant powder, the powder-added foams exhibited a decreasing trend for thermal conductivity, and the minimum was 0.048 w/(m·k), which indicated that the addition of plant powder can help to enhance the thermal insulation of composite foam. More importantly, the results of leaching experiment showed that the leaching rate of heavy metal cadmium in the composite foam with 50% plant powder content was as low as 0.14% after being immersed in the acidic (pH = 3) solution for 5 days, which implies that the foam materials are very safe. This study provides a new way to realize high value-added resource utilization of heavy metal-enriched plants.
Keywords: cadmium-rich plant; composite foams; high cadmium immobilization rate; low thermal conductivity.