Ultra-high-performance fiber-reinforced cementitious composite (UHPFRC) is used in orthotropic steel deck (OSD) to form a lightweight composite deck structure (LWCD), which is expected to solve the problems of fatigue cracking of traditional steel deck and pavement damage. This paper aims to study the influence of key design parameters on longitudinal bending and transverse fatigue performance, as well as the ultimate bearing capacity calculation theory of the LWCD. A local finite-element (FE) model was built to evaluate the vehicle-induced stress ranges of six typical fatigue-prone details. In total, eight negative bending tests on steel-UHPFRC composite beams and one fatigue test on a steel-UHPFRC composite plate were conducted to investigate the longitudinal bending performance and the transverse flexural fatigue behavior of the LWCD, respectively. The results show that adding a 60-mm UHPFRC layer can significantly reduce the stress amplitude of six typical fatigue details by 44.8% to 90%. The failure mode of the longitudinal bending tests is the U-rib buckle and all UHPFRC layers exhibit multiple cracking behaviors when the specimens failed. The longitudinal cracking stresses of the specimens are between 20.0 MPa to 27.3 MPa. The reinforcement ratio and cover thickness have a great influence on the cracking stress. While the ultimate bearing capacity of specimens with different parameters has little difference. The calculation method of the ultimate bearing capacity of a steel-UHPFRC composite structure is proposed. When the strain at the bottom of the u-rib is taken as 1.2 times the design yield strain, the calculated results are in good agreement with the experimental results. No fatigue failure was observed after 66.12 million fatigue cycles under the design load, highlighting the favorable fatigue resistance of the proposed LWCD.
Keywords: bending test; cracking stress; fatigue test; lightweight composite deck (LWCD); orthotropic steel deck (OSD).