To achieve the new level of blended cement performance, the slurries of Class C and F fly ash were mechano-chemically activated in a vibro-mill with superplasticizer and nanosilica. The resulting activated products were tested in mortars replacing up to 30% portland cement. The activation process resulted in the formation of nano-seed clusters and micronized ash particles that both significantly improve the early strength of mortars as well as allow for the replacement of portland cement with industrial by-products. A small amount, 0.1% (of a binder weight), of nanosilica was used in selected compositions to improve the process of activation and facilitate the formation of nano-seeds. Due to an intensive activation of fly ash in the vibro-mill and the formation of nano-seed hydration products, the increase in the heat of the hydration flux and improvement of the mechanical properties such as compressive strength, especially in the early stages of hardening, were achieved. It is envisioned that fly ash activation and the use of supplementary cementitious materials as a precursor can induce a denser structure of cementitious matrix due to better particle packing realized with the application of the nano-seed product, nanosilica, ultra-fine particles of fly ash, and the formation of a refined C-S-H structure realized with the incorporation of the nano-seed particles.
Keywords: activation; blended cement; cementitious; fly ash; hydration; matrix; nano-seed; nanosilica; strength; structure; top-down; vibro-mill.