Twins are generally regarded as obstacles to dislocations in face-centered cubic metals and can modify individual dislocations by locking them in twin boundaries or obliging them to dissociate. Through in situ tensile experiments on Al thin film in a transmission electron microscope, we report a dynamic process of dislocations being transported by twin lamella via periodic twinning and detwinning at the atomic scale. Following this process, a 60° dislocation first transforms into a sessile step of the twin boundary, then migrates under stress as a step and finally reverts back into a 60° dislocation. Our results reveal a novel evolution route of dislocations by a dislocation-twin interaction where the twins act as transport vehicles rather than as obstacles. The potential implications of this mechanism on toughening are also discussed.
Keywords: Al; Dislocation; crack tip; in situ transmission electron microscopy; twin.